| Suitable for synthesis of PU elastomer, PU foam, PU resin. |
|
Articles
|
component
|
water content WT%
|
acid value mgKOH/g
|
OH value mgKOH/g
|
color APHA
|
functionality
|
|
PO-6030
|
AA/BG
|
<0.05
|
<0.5
|
35-39
|
<80
|
diol
|
|
PO-6020
|
AA/BG/EG
|
<0.05
|
<0.8
|
52-60
|
<80
|
diol
|
|
PO-6120
|
AA/BG/EG
|
<0.05
|
<0.8
|
52-60
|
<80
|
diol
|
|
PO-6010
|
AA/BG/EG
|
<0.05
|
<0.8
|
105-115
|
<80
|
diol
|
|
PO-5010
|
AA/DEG
|
<0.05
|
<0.8
|
105-115
|
<100
|
diol
|
|
PO-7115
|
AA/DEG/EG
|
<0.05
|
<0.8
|
71-77
|
<100
|
diol
|
|
PO-7120
|
AA/DEG/EG
|
<0.05
|
<0.8
|
52-60
|
<100
|
diol
|
|
PO-7020
|
AA/DEG/EG
|
<0.05
|
<0.8
|
52-60
|
<100
|
diol
|
|
PO-7023
|
AA/DEG/TMP
|
<0.05
|
<0.8
|
52-60
|
<100
|
triol
|
|
PO-9003
|
CASTOR
|
<0.05
|
<0.8
|
140-160
|
-
|
multiol
|
|
PO-9103
|
CASTOR
|
<0.05
|
<0.8
|
140-160
|
-
|
multiol
|
|
| Suitable for water-proof coating, abrasion-resist coating, Industrial roller, industrial parts, pipe etc. |
|
Articles
|
Soild Content(%)
|
NCO(%)
|
MOCA(%)
|
Hardness(shore A)
|
Applications
|
|
SB-230
|
100
|
2.3
|
6.5-6.7
|
20
|
Hardner for waterproof
|
|
SB-260
|
100
|
2.6
|
7.4-7.6
|
25
|
Hardner for sealant or waterproof
|
|
SB-320
|
100
|
3.2
|
8.8-9.2
|
30
|
Hardner for sealant. For bridge,
airport
|
|
SB-600
|
100
|
6.0
|
17-17.5
|
45-55
|
Tennis court gymnasium, sport
ground.
|
|
SB-080
|
100
|
8.0
|
22.5-23
|
75-80
|
color seamless floor for hospital
|
|
SB-420
|
100
|
4.2
|
12-12.5
|
90
|
High Re-bound, good abrasion.
For bar rod, pipe; friction wheels,
L-100 equivalent. |
|
SB-630
|
100
|
6.3
|
18-18.5
|
95
|
High Re-bound, hydrolysis
resistance, high hardness. For roller, wheels, L-167 equivalent.
|
|
SB-800
|
100
|
8.0
|
22.5-23
|
99
|
High Re-bound, hydrolysis
resistance, high hardness, For roller, wheels, L-200 equivalent.
|
|
SB-920
|
100
|
9.2
|
25.5-26
|
72D
|
High resilience, heat resistance.
For high speed elastomer roller,
L-325 equivalent. |
|
SB-430
|
100
|
4.3
|
12-12.5
|
90
|
Good resilience, abrasion,
reasonable cost. For roller skate
|
|
SB-400
|
100
|
4.0
|
11.5-12
|
90
|
Excellent abrasion for roller
|
|
SB-410
|
100
|
4.1
|
11.7-12.3
|
90
|
Hydrolysis resistance for
roller
|
|
| Hardner
| Adhesives | PU
Resins for Shoe Sole | PU Resins for synthetic
leather | Polyester Polyols |
PU resins for elastomer |
|
|
 |
 |
 |
 |
 |
 |
 |
 |
 |
|||||||
|